A series of specimens with differen

A series of specimens with different surface morphology, pre-sintering process, and sintering temperature were designed for studying the improvement of bond strength between zirconia framework and veneering porcelain. Shear strength test, Scanning Electron Microscope (SEM), and Energy Dispersive Spectrometer (EDS) were adopted in the investigation. A remarkably enhance of average bond strength from 24.1 MPa to 37.2 MPa was obtained by performing humps on zirconia substrate. Moreover, a pre-sintering process for bonding porcelain was beneficial to the increasing of bond strength. Hence, during all-ceramic dental restoration fabrication, it is promising to perform surface treatment on zirconia and conduct pre-sintering procedure on bonding porcelain for the improvement of bond strength between zirconia framework and veneering porcelain.

結果 (繁體中文) 1:

用不同的表面形態的一系列試樣，預燒結過程中，燒結溫度被設計用於研究的粘結強度的氧化鋯框架和飾面瓷之間的改善。剪切強度試驗，掃描電子顯微鏡（SEM）和能譜儀（EDS）在調查中獲得通過。一個非常從24.1兆帕37.2兆帕物通過氧化鋯基板上進行隆起得到提高的平均粘結強度。此外，用於接合一瓷預燒結過程是粘結強度增加有益。因此，全瓷牙科修復在製造期間，它是有希望的，以於接合瓷器上的氧化鋯和行為預燒結過程進行表面處理的粘結強度的氧化鋯框架和飾面瓷之間的改善。

結果 (繁體中文) 2:

設計了一系列不同表面形態、燒結工藝和燒結溫度的標本，用於研究氧化矽框架與貼花瓷之間粘結強度的提高。在調查中採用了剪切強度試驗、掃描電子顯微鏡（SEM）和能源分散光譜儀（EDS）。通過在氧化矽基板上執行駝峰，平均粘結強度從24.1MPa顯著增強到37.2 MPa。此外，粘接瓷器的預燒結工藝有利於粘結強度的增強。因此，在全陶瓷牙科修復製造過程中，有希望對氧化矽進行表面處理，並進行粘接瓷器的預燒結程式，以改進氧化矽框架與貼面之間的粘結強度瓷。

結果 (繁體中文) 3:

設計了一系列不同表面形貌、預燒結工藝和燒結溫度的試件，研究了氧化鋯骨架與飾面瓷結合强度的提高。採用抗剪强度試驗、掃描電鏡（SEM）和能譜儀（EDS）進行了研究。在氧化鋯基體上進行駝峰處理，使平均結合强度從24.1兆帕顯著提高到37.2兆帕。此外，採用預燒結工藝結合陶瓷有利於提高結合强度。囙此，在全瓷修復體的製備過程中，對氧化鋯進行表面處理，對粘結瓷進行預燒結處理，以提高氧化鋯骨架與飾面瓷的粘結强度是很有希望的。