The 60 wt% Pt–Ru catalysts supporte

The 60 wt% Pt–Ru catalysts supported on the activated carbons, Pt–Ru/AC, with a Pt:Ru ratio of 1:1 atomic were prepared using the pretreated activated carbons. The precursors of active metals were H2PtCl6 · H2O and RuCl3· xH2O from Alfa Aesar. Re-activated activated carbons were suspended and stirred in distilled water for 2 h, and the RuCl3·xH2O aqueous solution was added slowly to the activated carbon slurry followed by H2PtCl6 · H2O aqueous solution. These mixtures were reduced by modiGed borohydride method [4], and then washed repeatedly with distilled water till the pH of the Gltered water became lower than 7.5. Finally, dried at 120◦C for 12 h in the air condition.

結果 (繁體中文) 1:

使用預處理的活性炭製備1原子：1 Ru比：支撐在活性炭，鉑釕/ AC，具有Pt 60％（重量）鉑釕催化劑。活性金屬的前體是氯鉑酸·H2O和將RuCl 3·從阿法埃莎xH2O的。再活化的活性炭懸浮並在蒸餾水中攪拌2小時，並且將RuCl 3·xH2O的溶液緩慢加入到活性炭的漿液，接著氯鉑酸·H2O水溶液水溶液。這些混合物通過modiGed硼氫化方法[4]還原，然後用蒸餾水反复洗滌，直至水Gltered的pH值變成低於7.5。最後，在乾燥120◦C在空氣條件12小時。

結果 (繁體中文) 2:

60 wt% Pt_Ru 催化劑支援活性炭 Pt_Ru/AC，Pt：Ru 比為 1：1 原子，使用預處理的活性炭製備。活性金屬的前體為H2PtCl6 |H2O 和 RuCl3*xH2O 來自阿爾法·艾薩爾。重新啟動的活性炭懸浮在蒸餾水中攪拌2小時，將RuCl3_xH2O水溶液緩慢地添加到活性炭漿中，然後加入H2PtCl6 |H2O 水溶液。這些混合物通過修改的硼氫化物法[4]減少，然後用蒸餾水反復清洗，直到玻璃水的pH低於7.5。最後，在120°C條件下乾燥12小時。

結果 (繁體中文) 3:

以預處理活性炭為載體，製備了Pt-Ru/AC催化劑，Pt:Ru原子比為1:1。活性金屬的前驅體為Alfa Aesar的H2PtCl6·H2O和RuCl3·xH2O。將重活性炭懸浮於蒸餾水中攪拌2小時，在活性炭漿中緩慢加入RuCl3·xH2O水溶液，再加入H2PtCl6·H2O水溶液。用改進的硼氫化法[4]還原這些混合物，然後用蒸餾水反復洗滌，直到所得水的pH值低於7.5。最後，在120℃下在空調中乾燥12小時。