Thanks Derek, glad to see 4k data l

Thanks Derek, glad to see 4k data looks ok, I have a few questions before our meeting this evening:

1. Overall, after the HTHH test, the pump PQ curve “rotated” to a “higher flow lower pressure” shape, though the "area under curve” is probably similar to
initial test. This indicates that the actuator has changed shape— even after it’s been cooled down to room temperature. Any inspection data on this?

2. Have you plotted some "Q vs noise” or P vs noise” curves for these 20 pumps to see if there is a correlation between noise and performance?

3. Are pumps in this lot using a new batch of pzt material compared to previous 4core modules?

4. Have you ever tried to use one PZT core, and package it in both “machined” housing and “molded” housing, to confirm that the packaging of the
cores is indeed the cause of performance increase?

結果 (繁體中文) 1:

由於德里克，很高興見到4K數據看起來不錯，我有我們的會議之前今晚幾個問題：

1。總體而言，HTHH試驗後，泵PQ曲線“旋轉”到一個“更高的流量低壓”的形狀，雖然“曲線下面積”可能是類似於
最初的測試，這表明該驅動器發生了變化，它已經冷卻至室溫後，即使形狀- 。所有檢查數據說明嗎？

2.你繪製一些“Q VS噪音”或P VS這些20泵噪聲“曲線，以查看是否有噪聲和性能之間的相關性？

3.是否使用PZT材料的新一批相比前4core模塊在這個地段泵？

4.你有沒有試過用一個PZT核心，並將其打包在兩個“加工”住房和“成型”的住房，以確認包裝
芯確實是業績增長的原因是什麼？

結果 (繁體中文) 2:

感謝德里克，很高興看到4k資料看起來不錯，我有幾個問題之前，我們今晚的會議：

1. 總體而言，在 HTHH 測試後，泵 PQ 曲線"旋轉"到"高流量較低壓力"形狀，但"曲線下的面積"可能類似于
初始測試。這表明，即使將執行器冷卻到室溫，其形狀也發生了變化。有這方面的檢查資料嗎？

2. 您是否為這 20 個泵繪製了一些"Q 與雜訊"或 P 與雜訊曲線，以查看雜訊和性能之間是否有相關性？

3. 與前一批 4 芯模組相比，此批次中的泵是否有使用新一批 pzt 材料？

4. 您是否曾經嘗試過使用一個 PZT 內核，並將其封裝在"加工"外殼和"模制"外殼中，以確認包裝的
核心確實是性能提升的原因嗎？

結果 (繁體中文) 3:

謝謝Derek，很高興看到4K數據看起來不錯，在今晚的會議之前我有幾個問題：
一。總的來說，在高溫高壓試驗之後，泵的pq曲線“旋轉”成“高流量低壓力”的形狀，儘管“曲線下面積”可能與
初始測試。這表明執行機構已經改變了形狀-即使是在冷卻到室溫之後。有這方面的檢查數據嗎？
2.你是否繪製了這20臺泵的“q vs noise”或“p vs noise”曲線，以確定譟音與效能之間是否存在相關性？
三。與之前的4芯模塊相比，這批泵是否使用了一批新的PZT資料？
四。你有沒有試過使用一個壓電陶瓷芯，並將其包裝在“機加工”外殼和“模壓”外殼中，以確認
覈心確實是效能提高的原因？