In this study, a series of specimen

In this study, a series of specimens with zirconia substrate and veneering porcelain were prepared. Different surface morphology, presintering process, and sintering temperature were designed. The shear strength test indicated that, the striations made no obvious difference to bond strength, while humps on zirconia substrate could obviously enhanced the bond strength between zirconia substrate and veneering porcelain. Due to the element diffusion, which was confirmed by Energy Dispersive Spectrometer (EDS), the bond strength was increased by a pre-sintering process for bonding porcelain.

結果 (繁體中文) 1:

在這項研究中，一系列與氧化鋯基板和飾面瓷試樣製備。不同的表面形態，預燒結過程中，和燒結溫度設計。剪切強度測試表明，所述條紋由無明顯差異的粘結強度，而氧化鋯基板上的隆起能明顯增強的氧化鋯基板和飾面瓷之間的粘合強度。由於該元件的擴散，這是由能量色散光譜儀（EDS）確認，則粘合強度增加了用於結合瓷預燒結過程。

結果 (繁體中文) 2:

在這項研究中，製備了一系列具有氧化矽基質和貼花瓷的標本。設計了不同的表面形態、預燒工藝和燒結溫度。剪切強度試驗表明，這種條紋對粘結強度沒有明顯影響，而氧化矽基板上的駝峰可以明顯增強氧化矽基材與貼花瓷之間的粘結強度。由於能量分散光譜儀（EDS）確認的元素擴散，粘結強度通過粘結瓷器的預燒結工藝增加。

結果 (繁體中文) 3:

在本研究中，我們製備了一系列以氧化鋯為基底的貼面瓷試件。設計了不同的表面形貌、預燒工藝和燒結溫度。抗剪强度試驗表明，紋路對粘結强度無明顯影響，而氧化鋯基底上的凸起明顯提高了氧化鋯基底與飾面瓷的粘結强度。利用能量色散譜儀（EDS）證實了元素擴散的存在，通過預燒結合工藝提高了陶瓷的結合强度。